High Flexural Strength Square Ceramic Tube Zirconia Material High Hardness
Tag Key words : Square Ceramic Tube
Square Ceramic Tube has very high hardness, very high stiffness, very good corrosion resistance to chemicals at high temperature, and very high refractoriness or use temperature. They may be used for a variety of electrical, mechanical, and thermal applications. They may be used as setter plates for firing parts in a kiln. The may be used for high temperature furnaces and as high temperature refractory turntables. Square Ceramic Tube may also be used for jewelry or for applications requiring high wear or abrasion resistance. Your imagination is the only limiting factor in the spectrum of possible applications for this component. Be sure to view all photos as they are an integral component of the item description.
Specific Gravity or Density: 3.9 g/cm3
Water Absorption or Porosity: 0%
Fusion Temperature or Melting Temperature: 2000 °C or 3632 °F
Maximum Working Temperature: 1800 °C or 2800 °F
Thermal Conductivity: 25 W/m* K
Specific Heat: 0.9 J/g*K
Expansion Coefficient or CTE: 7.5 x 10 E-6 inches/°C
Electrical Resistivity at 20 C: 10 E14 Ohm*cm
Electrical resistance at 600 C: 10 E8 Ohm*cm
Modulus of Elasticity: 44 x 10 E6 p.s.i. or 350 GPa.
| Product Name | High Flexural Strength Square Ceramic Tube Zirconia Material High Hardness |
| Material | zirconia |
| Color | White, Black , Blue , Yellow |
| OD | 0.2mm - 200mm, And According to drawings |
| Length | 5mm - 400mm, And According to drawings |
| Surface Roughness | Ra0.05 |
| Torlerance | +/- 0.001mm |
| Lead time: | 15 days |
| Max. working temperature | 1500 -2800 °C |
| Samples | Avaliable |
| Shipping: | Air Express (DHL/UPS/TNT/ FedEx) or Ocean Shipping |
Material Service:
Zirconia Ceramic: Mg-PSZ, Y-TZP, ZTA
Alumina Ceramic: 96%, 99%, 99.5% Al2O3
Silicon Nitride: Si3N4, RBSN, SRBSN, GPSN
Machinable Ceramic: Macor Ceramic
Machining Service:
Laser Cutting
CNC Machining
Cernerless Grinding and Inside Hole Honing
Surface Grinding and Polishing
Properties Sheet of zirconia and alumina :
| Properties | Units | 95 Alumina | 99 Alumina | ZrO2 |
| Density | g / cm³ | 3.65 | 3.92 | 5.95-6.0g/cm³ |
| Water absorption | % | 0 | 0 | 0 |
| Coefficient of thermal expansion | 10-6/K | 7.9 | 8.5 | 10.5 |
| Modulus of Elasticity Young's Mod | GPa | 280 | 340 | 210 |
| Poisson's ratio | / | 0.21 | 0.22 | 0.3 |
| HV Hardness HV | MPa | 1400 | 1650 | 1300-1365 |
| Flexural Strength @ room temperature | MPa | 280 | 310 | 950 |
| Flexural Strength @700°C | MPa | 220 | 230 | 210 |
| Compressive Strength @ room temperature | MPa | 2000 | 2200 | 2000 |
| Fracture Toughness | MPa *m 1/2 | 3.8 | 4.2 | 10 |
| Heat conductivity @ room temperature | W/ m*k | 18-25 | 26-30 | 2-2.2 |
| Electrical Resistivity @ room temperature | Ω*mm2 /m | >1015 | >1016 | >1015 |
| Max use temperature | °C | 1500 | 1750 | 1050 |
| Resistance to acid alkaline | / | high | high | high |
| Dielectric Constant | / | 9.5 | 9.8 | 26 |
| Dielectric Strength | KV/mm | 16 | 22 | / |
| Thermol Shock Resistance | △ T ( °C ) | 220 | 180-200 | 280-350 |
| Tensile Strength @ 25 °C | MPa | 200 | 248 | 252 |
Delivery:
Custom OEM will be shipped within 15 days after determining the parameters
The samples will be shipped within 3 days
Quick Delivery Via Fedex,DHL,UPS,TNT Etc.
Support customer to designate shipping company
For more informations (the price,delivery time,moq etc)about the ceramic plates, please contact us or email:admin@cerampart.com
CEO: Admin deng
Dongguan Mingrui Ceramic Tech. Co. Ltd.
Add: No.21 Chuangxing Rd., 2nd Industrial Zone of Shangsha,
Chang'an town, Dongguan city, Guangdong, China 523867
Email: admin@cerampart.com
FAQ
1. Monthly Capacity: 50,000-60,000 pcs;
2. Material: OEM or as per your suggestion;
3. Lead time: about 7-20 days, pls confirm the quantities required;
4. Incoterm: FOB, CFR, CIF;
5. Delivery Cost: It is determinated by the destination port;
6. Payment Term: PayPal; T/T; L/C.
7. Shipment: by sea, by air, by courier, by post, etc.